The main composition of refractory brick

Date:2017-08-15 15:46 From:Zhengzhou Sunrise Refractory Author:admin
The mineral composition of refractory brick is mainly kaolinite (Al2O3 · 2SiO2 · 2H2O) and 6% ~ 7% impurities (potassium, sodium, calcium, titanium, iron oxide). Select the high density, low water absorption of raw materials,  a reasonable level of preparation is the key to make low porosity refractory brick. Refractory brick is made with 50% soft clay and 50% hard clay clinker according to certain granularity requirements. After molding and drying,  firing under high temperature of 1300 ~ 1400 ℃.
The firing process is mainly due to the process of crystallization of mullite (3Al2O3 · 2SiO2). The SiO2 and Al2O3 in the refractory brick form a eutectic and low melting point silicate with the impurity during the firing process, surrounded by mullite crystals. The maximum temperature in the firing process is usually controlled at 1350 ° C to 1380 ° C, and the firing temperature of the low porosity fire clay brick (1420 ° C) is increased. The shrinkage of refractory brick is slightly increased, so that the density of   increases slightly and the low porosity is decline.
Refractory brick do not use the same kind of mud to use different appliances, fire mud selection of cleaning water, accurate weighing modulation, uniform mixing, tune the mud can not be arbitrarily diluted with water, mortar fullness is greater than 95% or more, ensure solid brick joints, the surface brick seam jointing with virgin pulp, the shell can not correct the parts with mud.
Refractory brick has a certain shape and scale of refractory material, large unit volume weight, large density, indicating that the density is good, the strength may be high, also known as high temperature load deformation temperature, called the burner change or called the residual line change, refers to each time the equal temperature change in the volume swell shrink, high temperature resistance, the  load softening temperature is at 1620 ° C-1640 ° C, thermal expansion coefficient is small.


Inquiry:

If you have any questions or good suggestions on our products and site, or if you want to know more information about our products, please write them and send to us, a representative will contact you within one business day. We guarantee that your information will not be divulged to the third party.

Title:
Name:
Tel:
*E-mail:
Country or Region:
*Message:
    
If you're interested in the product, please submit your requirements and contacts and then we will contact you in one day. We promise that all your informations won't be leaked to anyone.